Lean austenitic stainless steel

ABSTRACT

An austenitic stainless steel composition including relatively low Ni and Mo levels, and exhibiting corrosion resistance, resistance to elevated temperature deformation, and formability properties comparable to certain alloys including higher Ni and Mo levels. Embodiments of the austenitic stainless steel include, in weight percentages, up to 0.20 C, 2.0-9.0 Mn, up to 2.0 Si, 15.0-23.0 Cr, 1.0-9.5 Ni, up to 3.0 Mo, up to 3.0 Cu, 0.05-0.35 N, (7.5(C))≦(Nb+Ti+V+Ta+Zr)≦1.5, Fe, and incidental impurities.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation application claiming priority under35 U.S.C. §120 to U.S. patent application Ser. No. 12/610,577, filedNov. 2, 2009, now U.S. Pat. No. 8,337,749 which in turn claims priorityunder 35 U.S.C. §120 as a continuation-in-part of U.S. patentapplication Ser. No. 12/034,183, filed Feb. 20, 2008, now U.S. Pat. No.8,337,748 and which in turn claims priority to U.S. Provisional PatentApplication Ser. No. 61/015,264, filed Dec. 20, 2007.

BACKGROUND

1. Field of Technology

The present disclosure relates to an austenitic stainless steel. Inparticular, the present disclosure relates to a cost-effectivestabilized austenitic stainless steel composition including, inter alia,a low Ni level, no more than an incidental level of Mo, high yieldstrength, and at least comparable corrosion resistance and hightemperature properties relative to certain higher Ni austenitic alloyssuch as, for example, T-321 alloy (UNS S32100).

2. Description of the Background of the Technology

Austenitic stainless steels exhibit a combination of highly desirableproperties that make them useful for a wide variety of industrialapplications. These steels possess a base composition of Fe that isbalanced by the addition of austenite-promoting and stabilizingelements, such as Ni, Mn, and N, to allow additions of ferrite-promotingelements, such as Cr and Mo, which enhance corrosion resistance, to bemade while maintaining an austenitic structure at room temperature. Theaustenitic structure provides the steel with highly desirable mechanicalproperties, particularly toughness, ductility, and formability.

A specific example of an austenitic stainless steel is AISI Type 316stainless steel (UNS S31600), which is a 16-18% Cr, 10-14% Ni, and 2-3%Mo-containing alloy. The ranges of alloying ingredients in this alloyare maintained within the ranges specified in order to maintain a stableaustenitic structure. As is understood by one skilied in the art, Ni,Mn, Cu, and N contents, for example, contribute to the stability of theaustenitic structure. However, the rising costs of Ni and Mo havecreated the need for cost-effective alternatives to S31600 which stillexhibit high corrosion resistance and good formability.

Another alloy alternative is Grade 216 (UNS S21600), which is describedin U.S. Pat. No. 3,171,738. S21600 contains 17.5-22% Cr, 5-7% Ni, 7.5-9%Mn, and 2-3% Mo. Although S21600 is a lower Ni, higher Mn variant ofS31600, the strength and corrosion resistance properties of S21600 aremuch higher than those of S31600. However, as with the duplex alloys,the formability of S21600 is not as good as that of S31600. Also,because S21600 contains the same amount of Mo as does S31600, there isno cost savings for Mo.

A variant of S31600 also exists which is primarily intended for use athigh temperatures. This alloy is designated as Type 316Ti (UNS S31635).The significant difference between S31600 and S31635 is the presence ofa small addition of titanium balanced to the amount of C and N presentin the steel. The resulting steel, S31635, is less prone to thedeleterious formation of Cr carbides at elevated temperatures and duringwelding, a phenomenon known as sensitization. Such additions can alsoenhance elevated temperature properties due to the strengthening effectsof primary and secondary carbide formation. The specified range fortitanium in S31635 is given by the following equation:[5×(% C+% N)]≦Ti≦0.70%.However, S31635 uses costly raw matenal.

Another example of an austenitic stainless steel is Type 321 stainlesssteel (UNS S32100), which includes, in weight percentages, 17.00-19.00%Cr, 900-12.00% Ni, up to 2.00% Mn, up to 0.08% C, up to 0.75% Si, [5×(%C+% N)]≦Ti≦0.70%, up to 0.045% P, up to 0.030% S, up to 0.10% N, andbalance Fe. Type 321 alloy is stabilized against Cr carbide formation bythe addition of titanium balanced to the amount of C and N present inthe steel. Although Type 321 alloy does not lnciude an intentionaladdition of Mo, it does include a significant level of costly alloyingelements.

Other examples of alloys include numerous stainless steels in which Niis replaced with Mn to maintain an austenitic structure, such as ispracticed with Type 201 steel (UAS S20100) and similar grades. However,a need remains for a corrosion resistant, lower cost alternative torelatively highly alloyed austenitic stainless steels such as Type 321alloy and that provides at least comparable strength and hardnessproperties to Type 321 alloy.

SUMMARY

Accordingly, the alloy according to the present disclosure provides asolution that is not currently available in the marketplace, which is astabilized austenitic stainless steel alloy composition exhibiting atleast comparable corrosion resistance, strength, and hardness propertiesrelative to Type 321 austenitic stainless steel, while providing asignificant raw material cost savings relative to Type 321 alloy.Accordingly, the present alloy is a stabilized austenitic stainlesssteel that includes controlled levels of carbide-forming elements toimprove corrosion resistance and elevated temperature properties. Thepresent alloy also includes combined levels of Mn, Cu, and N sufficientto provide an alloy exhibiting certain properties, at least similar tothose of higher Ni alloys, but at a significantly lower raw materialcost.

The alloy according to the present disclosure is an austenitic stainlesssteel that uses a combination of Mn, Cu, and N as substitutes for themore costly element Ni. The result is an alloy having lower cost and atleast comparable formability, corrosion resistance, and elevatedtemperature strength properties relative to, for example, Type 321.Embodiments of the alloy according to the present disclosure may befabricated to light gauge, and include a clean microstructure withrelatively fine grains to enhance formability.

An embodiment of the ahoy according to the present disclosure isdirected to an austenitic stainless steel including, in weightpercentages, up to 0.20 carbon (C), 2.0 to 9.0 manganese (Mn), up to 2.0silicon (Si), 15.0 to 23.0 chromium (Cr), 1.0 to 9.5 nickel (Ni), up to3.0 molybdenum (Mo), up to 3.0 copper (Cu), 0.05 to 0.35 nitrogen (N),(7.5(% C))≦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)≦1.5,iron (Fe), and incidental impurities. Certain embodiments of theaustenitic stainless steel may include up to 0.01% boron (B). Certainembodiments may include at least 0.1% niobium, or may include niobium ina concentration of at least (7.5(% C)).

Another embodiment according to the present disclosure is directed to anaustenitic stainless steel, comprising, in weight percentages, up to0.10 C, 2.0 to 8.0 Mn, up to 1.00 Si, 16.0 to 22.0 Cr, 1.0 to 7.0 Ni,0.10 to 2.0 Mo, up to 1.00 Cu, 0.08 to 0.30 N, (7.5(% C))≦(% niobium+%titanium+% vanadium+% tantalum+% zirconium)≦1.5, up to 0.040 phosphorus(P), up to 0.030 sulfur (S), Fe, and incidental impurities. Certainembodiments of the austenitic stainless steel may include up to 0.01% B.Certain embodiments may include at least 0.1% niobium, or may includeniobium in a concentration of at least (7.5(% C)).

An alternative embodiment according to the present disclosure isdirected to an austenitic stainless steel comprising, in weightpercentages, up to 0.08 C, 3.5 to 6.5 Mn, up to 1.00 Si, 17.0 to 21.0Cr, 3.0 to 6.0 Ni, 0.1 to 1.0 Mo, up to 1.0 Cu, 0.08 to 0.30 N, (7.5(%C))≦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)≦1.0, up to0.035 P, up to 0.005 S, Fe, and incidental impurities. Certainembodiments of the austenitic stainless steel may include up to 0.01% B,certain embodiments may include at least 0.1% niobium, or may includeniobium in a concentration of at least (7.5(% C)).

In certain embodiments, the austenitic stainless steel according to thepresent disclosure has one or more of a PRE_(N) value greater than 18, aferrite number less than 12, and an MD₃₀ value of less than 34° C.

One method of producing an austenitic stainless steel according to thepresent disclosure is by melting a charge in an electric arc furnace,refining in an AOD, casting into ingots or continuously cast slabs,reheating the ingots or slabs and hot rolling them to produce plates orcoils, cod rolling coils to a specified thickness, and annealing andpickling the material. Other methods of producing the invented materialmay also be used, including melting and/or re-melting in a vacuum orunder a special atmosphere, casting into shapes, or the production of apowder that is consolidated into slabs or shapes.

An austenitic, stainless steel according to the present disclosure maybe used in numerous applications. According to one example, alloys ofthe present disclosure may be included in articles of manufactureadapted for use in low temperature or cryogenic environments. Additionalnon-limiting examples of articles of manufacture that may be fabricatedfrom or include the present alloy are flexible connectors for automotiveand other applications, bellows, flexible pipe, chimney liners, and flueliners.

DETAILED DESCRIPTION

In the present description, other than in the operating examples orwhere otherwise indicated, all numbers expressing quantities orcharacteristics of ingredients and products, processing conditions, andthe like are to be understood as being modified in ail instances by theterm “about”. Accordingly, unless indicated to the contrary, anynumerical parameters set forth in the following description areapproximations that may vary depending upon the desired properties oneseeks to obtain in the product and methods according to the presentdisclosure. At the very least, and not as an attempt to limit theapplication of the doctrine of equivalents to the scope of the claims,each numerical parameter should at least be construed in light of thenumber of reported significant digits and by applying ordinary roundingtechniques. All numerical ranges stated herein include all sub-rangessubsumed therein. For example, a range of “1 to 10” is intended toinclude all sub-ranges between and including the recited minimum valueof 1 and the recited maximum value of 10.

Embodiments of the austenitic stainless steel according to the presentdisclosure will now be described in detail. In the followingdescription, “%” or “percent” refer to weight percentages, unlessotherwise specified. The present disclosure is directed to an austeniticstainless steel exhibiting at least comparable corrosion resistance,elevated temperature strength properties, and formability relative toType 321 alloy, and at lower overall cost of raw materials. Theaustenitic stainless steel composition may include, in weightpercentages, up to 0.20 C, 2.0 to 9.0 Mn, up to 2.0 Si, 15.0 to 23.0 Cr,1.0 to 9.5 Ni, up to 3.0 Mo, up to 3.0 Cu, 0.05 to 0.35 N, (7.5(% C))≦(%niobium+% titanium+% vanadium+% tantalum+% zirconium)≦1.5, Fe, andincidental impurities. Certain embodiments of the austenitic stainlesssteel may include up to 0.01 B. Certain embodiments of the austeniticstainless steel may inciude at least 0.1% niobium, or may includeniobium in, a concentration of at least (7.5(% C)).

Another embodiment of the invention is an austenitic stainless steel,including, in weight %, to 0.10 C, 2.0 to 8.0 Mn, up to 1.00 Si, 16.0 to22.0 Cr, 1.0 to 7.0 Ni, 0.10 to 2.0 Mo, up to 1.00 Cu, 0.08 to 0.30 N,(7.5(% C))≦(% niobium±% titanium+% vanadium+% tantalum+% zirconium)≦1.5,up to 0.040 P, up to 0.030 Si, Fe, and incidental impurities. Certainembodiments of the austenitic stainless steel may include up to 0.01 B.Certain embodiments of the austenitic stainless steel may include atleast 0.1% niobium, or may include niobium in a concentration of atleast (7.5(% C)).

According to an alternative embodiment, the present disclosure isdirected to an austenitic stainless steel including, in weightpercentages, up to 0.08 C, 3.5 to 6.5 Mn, up to 1.00 Si, 17.0 to 21.0Cr, 3.0 to 6.0 Ni, 0.5 to 1.0 Mo, up to 1.0 Cu, 0.08 to 0.30 N, (7.5(%C))≦(% niobium+% titanium+% vanadium+% tantalum+% zirconium)≦1.0, up to0.035 P, up to 0.005 S, Fe, and incidental impurities. Certainembodiments of the austenitic stainless steel may include up to 0.01 B.Certain embodiments of the austenitic stainless steel may include atleast 0.1% niobium, or may include niobium in a concentration of atleast (7.5(% C)).

C: Up to 0.20%

C acts to stabilize the austenite phase and inhibits thedeformation-induced martensitic transformation. However, C alsoincreases the probability of forming Cr carbides, especially duringwelding, which reduces corrosion resistance and toughness. Accordingly,the austenitic stainless steel of the present invention has up to 0.20%C. In an embodiment of the invention, the content of C may be 0.10% orless. Alternatively, the content C may be 0.08% or less, 0.03% or less,or 0.02% or less.

Si: Up to 2.0%

Having greater than Si promotes the formation of embrittling phases,such as sigma, and reduces the solubility of N in the alloy. Si alsostabilizes the ferritic phase, and greater than 2% Si requiresadditional austenite stabilizers to maintain the austenitic phase.Accordingly, in certain embodiments the austenitic stainless steel ofthe present invention has up to 2.0% Si. In embodiment of the invention,the Si content may be 1.0% or less, Si helps to minimize the reactivityof certain alloying elements with niobium and assists with phase balancein the alloy. In certain embodiments according to the presentdisclosure, the effects of Si addition are balanced by adjusting the Sicontent to 0.5-1.0%. In other embodiments, the effects of Si additionare balanced by adjusting the Si content to 0.1-0.4%. Alternatively, incertain embodiments according to the present disclosure the Si contentmay be 0.5% or less, 0.4% or less, or 0.3% or less.

Mn: 2.0-4.0%

Mn stabilizes the austenitic phase and generally increases thesolubility of N, a beneficial alloying element. To sufficiently producethese effects, a Mn content of not less than 2.0% is required. Both Mnand N are effective substitutes for the more expensive element, Ni.However, having greater than 9.0% Mn degrades the material's workabilityand its corrosion resistance in certain environments. Also because ofthe difficulty in decarburizing stainless steels with high levels of Mn,such as greater than 9.0%, high Mn levels significantly increase theprocessing costs of manufacturing the material. Accordingly, in order toproperly balance the corrosion resistance, phase balance, ductility andother mechanical, properties in the austenitic stainless steel of thepresent invention, the Mn level is set at 2.0-9.0%. In certainembodiments according to the present disclosure, the Mn content may be2.0-8.0%, 3.5-7.0%, or 7%.

Ni: 1.0-9.5%

The present inventors sought to limit the Ni content of the alloy whilemaintaining acceptable properties. At least 1% Ni is required to stabzethe austenitic phase with respect to both ferrite and martensiteformation. Ni also acts to enhance toughness and formability. However,due to the relatively high cost of Ni, it is desirable to keep the Nicontent as low as possible. Although Mn and N may be partial substitutesfor Ni, high levels of Mn and N will result in unacceptable levels ofwork hardening, reducing formability. Therefore, the ahoy must include aminimum concentration of Ni to provide for acceptable formability. Theinventors have found that 1.0-9.5% ramie of Ni can be used in additionto the other defined ranges of elements to achieve an alloy havingcorrosion resistance and formability as good as or better than those ofhigher Ni alloys. Accordingly, the austenitic stainless steel of thepresent invention has 1.0-9.5% nickel. In an embodiment, the Ni contentmay be 2.0-6.5%, or may be 3.0-6.0%.

Cr: 15.0-23.0%

Cr is added to impart corrosion resistance to stainless steels byforming a passive film on the ahoy surface. Cr also acts to stabilizethe austenitic phase with respect to martensitic transformation. Atleast 15% Cr is required to provide adequate corrosion resistance. Onthe other hand, because Cr is a powerful ferrite stabilizer, a Crcontent exceeding 23% requires the addition of more costly alloyingelements, such as Ni or cobalt, to keep the ferrite content acceptablylow. Having more than 23% Cr also makes the formation of undesirablephases, such as sigma, more likely. Accordingly, the austeniticstainless steel of the present invention has 15.0-23.0% Cr. In anembodiment, the Cr content may be 16.0-22.0%, or alternatively may be17.0-21.0%.

N: 0.05-0.35%

N is included in the present alloy as a partial replacement for theaustenite stabilizing element Ni and the corrosion resistance enhancingelement Mo. N also improves alloy strength. At least 0.05% N isnecessary for strength and corrosion resistance and to stabilize theaustenitic phase. The addition of more than 0.35% N may exceed thesolubility of N during melting and welding, which results in porositydue to N gas bubbles. Even if the solubility limit is not exceeded, a Ncontent of greater than 0.35% increases the propensity for theprecipitation of nitride particles, which degrades corrosion resistanceand toughness. The present inventors have determined that a N content upto 0.35% is compatible with the possible Nb levels in the alloy, withoutthe formation of a problematic level of niobium carbonitrideprecipitates. Accordingly, the austenitic stainless steel of the presentinvention has 0.05-0.35% N. In an embodiment, the N content may be0.08-0.30%, or alternatively may be 0.05-0.2%.

Mo: Up to 3.0%

The present inventors sought to limit the Mo content of the ahoy whilemaintaining acceptable properties. Mo is effective in stabilizing thepassive oxide film that forms on the surface of stainless steels andprotects against pitting corrosion by the action of chlorides. Incertain embodiments, the Mo content may be 0.1-3.0%, which is adequateto provide the required corrosion resistance in combination with theproper amounts of Cr and N. A Mo content exceeding 3.0% causesdeterioration of hot workability by increasing the fraction of ferriteto potentially detrimental levels. High Mo content also increases thelikelihood of forming deleterious intermetallic phases, such as sigmaphase. In addition, Mo is an expensive alloying element. Accordingly,the austenitic stainless steel composition of the present invention hasup to 3.0% Mo. In certain embodiments according to the presentdisclosure, the alloy includes no intentional addition of Mo. In otherembodiments, the Mo content may be 0.1-1.0%, or may be 0.5-1.0%.

B: Up to 0.01%

Additions as low as 0.0005% B optionally may be added to the ahoy of thepresent disclosure to improve the hot workability and surface quality ofstainless steels. However, additions of more than 0.01% B degrade thecorrosion resistance and workability of the alloy. Accordingly, certainembodiments of an austenitic stainless steel composition according tothe present disclosure may in up to 0.01% B. In an embodiment, the Bcontent may be up to 0.008%, or may be up to 0.005%. In anotherembodiment, the B content may be 0.001-0.003%

Cu: Up to 3.0%

Cu is an austenite stabilizer and may be used to replace a portion ofthe Ni in this alloy. It also improves corrosion resistance in reducing,environments and improves formability by reducing the stacking faultenergy. However, additions of more than 3% Cu have been shown to reducethe hot workability of austenitic stainless steels. Accordingly, theaustenitic stainless steel composition of the present invention has upto 3.0% Cu. In an embodiment, Cu content may be up to 1.0%. In anotherembodiment, Cu content may be 0.4-0.8%.

W: Up to 4.0%

W provides a similar effect to that of molybdenum in improvingresistance to chloride pitting and crevice corrosion. W may also reducetendency for sigma phase formation when substituted for molybdenum.However, additions of more than 4% may reduce the hot workability of thealloy. Accordingly, the austenitic stainless, steel composition of thepresent invention has up to 4.0% W. In an embodiment, W content may be0.05-0.60%.

1.0≦(Ni+CO)≦9.5

Nickel and cobalt both act to stabilize the austenitic phase withrespect to ferrite formation. At least 1% (Ni+Co) is required tostabilize the austenitic phase in the presence of ferrite stabilizingelements such as Cr and Mo, which must be added to ensure propercorrosion resistance. However, both Ni and Co are costly elements, so itis desirable to keep the (Ni+Co) content less than 9.5%. In anembodiment, the (Ni+Co) content may be greater than 4.0% but less than7.5%.

(7.5(% C))≦(% Nb+% Ti+% V+% Ta+% Zr)≦1.5

Niobium (Nb) reacts with C, and to a lesser extent N, to form carbidesand carbonitrides in the form of small particles. These particleseffectively prevent the formation of deleterious chromium carbidesduring elevated temperature service and during welding, which improvescorrosion resistance. These particles, when produced using an effectiveheat treatment, can also improve elevated temperature strength and creepresistance. A minimum addition of (7.5×% C) provides for one atom of Nbfor every one atom of C present dissolved in the metal. Higher levels ofNb will consume beneficial N, so it is desirable to keep the Nb contentless than 1.5%. Other elements which form stable carbides, including butnot limited to titanium (Ti), vanadium (V), tantalum (Ta), and zirconium(Zr) may be added in substitution for niobium. However, such substitutesreact more strongly with N than Nb and therefore are controlled toprovide a beneficial effect, such as improved weldabilty. The inventorshave determined that the sum of the weight percentages of Nb, Ti, V, Ta,and Zr should be maintained in the range of (7.5(% C)) up to 1.5%.Stated differently, (7.5(% C))≦(% Nb+% Ti+% V+% Ta+% Zr)≦1.5%. Incertain embodiments, (7.5(% C))≦(% Nb+% Ti+% V+% Ta % Zr)≦1.0%. Incertain preferred embodiments, the alloy includes at least 0.1% Nb, andthe sum of the weight percentages of Nb, Ti, V, Ta, and Zr is in therange of (7.5(% C)) up to 1.5% or 1.0%. In certain embodiments, Ti, V,Ta, and Zr are present only as incidental impurities or are maintainedat levels as low as practical. In certain embodiments, in order tooptimize corrosion resistance, elevated temperature strength, creepresistance, and weldabilty properties of the alloy, certain embodimentsof the alloy include a Nb content of at least (7.5(% C)), and Ti, V, Ta,and Zr are present only as incidental impurities. In certainembodiments, the Ti content may be less than 0.01%. Also, in certainembodiments, the Ti content may be 0.001-0.005%. The present inventorshave determined that a Nb content up to 1.5% is compatible with thealloy's N content of 0.05-0.35% in that the combination does not resultin a level of niobium carbonitride precipitates that unacceptablydegrades creep resistance.

In certain embodiments according to the present disclosure, the balanceof the stabilized austenitic stainless steel of the present inventionincludes Fe and unavoidable impurities, such as P and S. The unavoidableimpurities are preferably kept to the owest practical and economicaliyjustifiable level, as understood by one skilled in the art.

Elements that form very stable nitrides, such as Al, should be kept tolow levels.

The stabilized austenitic stainless steel of the present invention canalso be defined by equations that quantify the properties theyexexhibit, including, for example, pitting resistance equivalencenumber, ferrite number, and MD₃₀ temperature.

The pitting resistance equivalence number (PRE_(N)) provides a relativeranking of an alloy's expected resistance to pitting, corrosion in achloride-containing environment. The higher the PRE_(N), the better theexpected corrosion resistance of the ahoy. The PRE_(N) can be calculatedby the following formula:PRE_(N)=% Cr+3.3(% Mo)+16(% N)

Alternatively, a factor of 1.65(% W) can be added to the above formulato take into account the presence of tungsten in an ahoy. Tungstenimproves the pitting resistance of stainless steels and is about half aseffective as molybdenum by weight. When tungsten is included in thecalculation, the pitting resistance equivalence number is designated asPRE_(W), which is calculated by the following formula:PRE_(W)=% Cr+3.3(% Mo)+1.65(% W)+16(% N)

The alloy of the present invention has a PRE_(N) value of greater than18. In certain embodiments, the PRE_(N) value may be 18-24. In certainembodiments, the PRE_(N) value may be 18-22. In certain embodiments, thePRE_(N) value may be 20-22.

The alloy of the invention also may be defined by its ferrite number. Apositive ferrite number generally correlates to the presence of ferrite,which improves an alloy's solidification properties and helps to inhibithot cracking of the alloy during hot working and welding operations. Asmall amount of ferrite is thus desired in the initial solidifiedmicrostructure for good castability and for prevention of hot-crackingduring welding. On the other hand, too much ferrite can result inproblems during service, including but not limited to, microstructuralinstability, limited ductility, and impaired high temperature mechanicalproperties. The ferrite number can be calculated using the followingequation:FN=3.34(Cr+1.5Si+Mo+2Ti+0.5Cb)−2.46(Ni+30N+30C+0.5Mn+0.5Cu)−28.6The alloy of the present invention has a ferrite number of up to 12, andpreferably is a positive number. In certain embodiments according to thepresent disclosure, the ferrite number may be greater than 0 to 10, ormay be 1 to 4.

The MD₃₀ temperature of an alloy is defined as the temperature at whichcold deformation of 30% will result in a transformation of 50% of theaustenite to martensite. The lower the MD₃₀ temperature is, the moreresistant a material is to martensite formation. Resistance tomartensite formation results in a lower work hardening rate, whichresults in good formability, especially in drawing applications. MD₃₀ iscalculated according to the following equation:MD₃₀(° C.)=413−462(C+N)−9.2Si−8.1Mn−13.7Cr−9.5Ni−17.1Cu−18.5MoThe alloy of the present invention has an MD₃₀ temperature of less than34° C., preferably less than 10° C. In certain embodiments, the MD₃₀temperature may be less than −10° C. In certain embodiments, the MD₃₀temperature may be less than −20° C.

EXAMPLES Example 1

Table 1 includes the compositions and calculated parameter values forExperimental Alloys 1-5 and Comparative Alloys S31690, S31635, S21600,and S20100.

Experimental Alloys 1-5 were melted in a laboratory-size vacuum furnaceand poured into 50-lb ingots. These ingots were re-heated and hot rolledto produce material about 0.25″ thick. This material was annealed,blasted, and pickled. Some of that material was cold rolled to0.100″-thick, and the remainder was cold rolled to 0.050 or0.040″-thick. The cold rolled material was annealed and pickled.Comparative Alloys S31600, S31635, S21600, and S20100 were commerciallyavailable, when the testing was performed and the data shown for thesealloys were taken from published literature or measured from testing ofmaterial produced for commercial sale.

The calculated PRE_(W) values for each alloy are shown in Table 1. Usingthe equation discussed herein above, the alloys having a PRE_(W) greaterthan 24.0 would be expected to have better resistance to chloridepitting than Comparative Alloy S31635 material, while those having alower PRE_(W) would pit more easily.

The ferrite number for each alloy in Table 1 has also been calculated.The ferrite number for each of Experimental Alloys 1-5 is in the rangeof less than 10.

The MD₃₀ values were also calculated for the alloys in Table 1.According to the calculations, Experimental Alloys 1-5, particularlyExperimental Alloys 4 and 5, exhibit similar resistance to martensiteformation to Comparative Alloys S31600 and S31635.

TABLE 1 Experimental Alloys Comparative Alloys 1 2 3 4 5 S31600 S31635S21600 S20100 C 0.017 0.015 0.014 0.014 0.016 0.017 0.016 0.018 0.02 Mn4.7 4.8 4.7 5.1 4.9 1.24 1.81 8.3 6.7 Si 0.26 0.27 0.28 0.29 0.3 0.450.50 0.40 0.40 Cr 16.6 16.6 16.6 18.1 18.2 16.3 16.8 19.7 16.4 Ni 5.25.2 5.2 5.5 5.5 10.1 10.7 6.0 4.1 Mo 1.47 1.47 1.47 1.00 1.1 2.1 2.112.5 0.26 Cu 0.40 0.40 0.39 0.40 0.5 0.38 0.36 0.40 0.43 N 0.075 0.1040.081 0.129 0.170 0.04 0.013 0.37 0.15 P 0.011 0.012 0.012 0.014 0.0140.03 0.031 0.03 0.03 S 0.0010 0.0012 0.0012 0.0016 0.0016 0.0010 0.00040.0010 0.0010 W 0.10 0.10 0.09 0.04 0.09 0.11 0.10 0.10 0.1 B 0.00190.0018 0.0016 0.0022 0.0022 0.0025 0.0025 0.0025 0.0005 Fe Bal Bal BalBal Bal. Bal. Bal. Bal. Bal. Nb 0.710 0.498 0.288 0.500 0.26 0.35 0.020.10 0.10 Co 0.22 0.19 0.15 0.19 0.15 — — — — Ti — — — — — — 0.22 — — FN8.3 5.8 7.5 6.6 3.7 4.1 6.7 −6.2 −2.3 PRE_(W) 22.9 23.4 23.1 23.6 24.724.0 24.0 33.9 19.7 MD₃₀ 19.3 6.6 17.2 −22.2 −46.2 −63 −72.4 −217.4 0.7RMCI 0.63 0.63 0.62 0.59 0.60 0.96 1.00 0.80 0.41 Yield 47.0 47.0 46.148.4 53.7 43.5 41.5 55 43 Tensile 102.0 105.5 104.5 105.9 106.4 90.692.0 100 100 % E 43 49 48 41 40 56 67 45 56 OCH 0.42 0.39 0.40 0.41 0.430.45 — — —

Table 1 also shows a raw material cost index (RMCI), which compares thematerial costs for each alloy to that of Comparative Alloy S31635. TheRMCI was calculated by multiplying the average October 2007 cost for theraw materials Fe, Cr, Mn, Ni, Mo, W, and Co by the percent of eachelement contained in the alloy and dividing by the cost of the rawmaterials in Comparative Alloy S31635. As the calculated values show,each of Experimental Alloys 1-5 has an RMCI of less than 0.65, whichmeans the cost of the raw materials contained therein are less than 65%of those in Comparative Alloy S31635 based on the October 2007 costvalues. That a material could be made that has similar properties toComparative Alloy S31635 at a significantly lower raw material cost issurprising and was not anticipated from the prior art.

The mechanical properties of Experimental Alloys 1-5 have been measuredand compared to those of Comparative Alloys S31600, S31635, S21600, andS20100. The measured yield strength, tensile strength, percentelongation over a 2-inch gage length, and Olsen cup height are shown inTable 1. The tensile tests were conducted on 0.100″ gale material, theCharpy tests were conducted on 0.197″ thick samples, and the Olsen cuptests were run on material between 0.040- and 0.050-inch thick. Alltests were performed at room temperature. Units for the data in Table 1are as follows: yield strength and tensile strength, ksi: elongation,percent; Olsen cup height, inches. As can be seen from the data, theExperimental Alloys 1-5, and in particular Experimental Alloys 4 and 5,exhibited comparable properties to those of the S31635 material.Experimental Alloys 1-5, however, included less than half theconcentration of nickel and also significantly less molybdenum than inComparative Alloy S31635. The significantly lower concentration of thecostly alloying elements nickel and molybdenum is such that the RMCI ofComparative Alloys 4 and 5 is at least 40% less than for ComparativeAlloy S31635. Despite their substantially reduced levels of nickel andmolybdenum, however, Experimental Alloys 4 and 5 had an austeniticmicrostructure and exhibited yield and tensile strength significantlybetter than for Comparative Alloy S31635.

Example 2

Table 2 includes the compositions and calculated parameter values forExperimental Alloys 6-10 and Comparative Alloys S32100 and Type 216Cb.As shown in Table 2, Experimental Alloys 6-10 generally includeincreased levels of Mn, N, and Nb and reduced levels of Ni compared toComparative Alloy S32100. Experimental Alloys 6-10 also includedecreased levels of Mo compared to Comparative Alloy T216Cb andExperimental alloys 1-5.

Experimental Alloys 6-10 were melted in a laboratory size vacuum furnaceand poured into 50-lb ingots. These ingots were reheated and hot rolledto produce material about 0.250″ thick. This material was annealed,blasted, and pickled. Some of that material was cold rolled to 0.100″thick, and the remainder was cold rolled to 0.050″ or 0.040″ thick. Thecold rolled material was annealed and pickled. Comparative Alloy S32100is commercially available, and the data shown for this alloy was takenfrom published literature or measured from testing of material recentlyproduced for commercial sale. Comparative Alloy T216Cb is described inU.S. Patent Publication No. 2009-0162237 A1 (U.S. patent applicationSer. No. 12/034,183), and the data shown for this alloy was measuredfrom testing of material produced according to the description thereinor taken from published literature.

The calculated PRE_(N) values for each alloy are shown in Table 2. Usingthe equation discussed herein above, the alloys having a PRE_(N) greaterthan 18 would be expected to have better resistance to chloride pittingthan Comparative Alloy S32100 material, while those having a PRE_(N)lower than 24 would be expected to pit more readily than the material ofComparative Alloy T216Cb. The PRE_(N) values for each of ExperimentalAlloys 6-10 is in a preferred range of 18-24.

The ferrite number for each alloy in Table 2 has also been calculated.The ferrite number for each of Experimental Alloys 6-10 is in thepreferred range of less than 12. According to the calculations,Experimental Alloys 8-10 would exhibit improved formability compared toComparative Alloy S32100.

The MD₃₀ values were also calculated for the alloys in Table 2.According to the calculations, Experimental Alloys 6-10, andparticularly Experimental Alloys 3 and 5, would exhibit improvedresistance to martensite formation compared to Comparative Alloy S32100.

TABLE 2 Experimental Alloys Comparative Alloys 6 7 8 9 10 S32100 S32100T216Cb T216Cb C 0.017 0.017 0.017 0.019 0.017 0.017 0.017 0.016 0.02 Mn6.9 6.9 6.9 6.8 4.4 1.8 1.9 4.9 4.86 Si 0.34 0.35 0.34 0.33 0.16 0.550.52 0.3 0.36 Cr 18.3 18.2 18.2 16.7 18.2 17.3 18.2 18.2 18.02 Ni 5.04.0 3.5 3.0 4.5 9.3 9.4 5.5 5.54 Mo 0.30 0.30 0.30 0.30 0.29 0.35 0.251.1 0.92 Cu 0.52 0.52 0.52 0.52 0.62 0.32 0.23 — — N 0.051 0.094 0.1710.149 0.183 0.011 0.011 0.17 0.17 P 0.020 0.020 0.020 0.021 0.020 0.0280.027 0.014 0.024 S 0.0019 0.0018 0.0000 0.0000 0.0013 0.0001 0.00080.0016 0.0005 B 0.0026 0.0018 0.0025 0.0024 0.0024 — 0.0030 — — Fe BalBal Bal Bal Bal. Bal. Bal. Bal. Bal. Nb 0.26 0.26 0.26 0.26 0.26 0.030.00 0.26 0.23 Ti 0.004 0.004 0.004 0.004 0.004 0.187 0.047 — — FN 9.18.1 3.8 1.5 2.3 6.6 8.2 4.5 3.2 PRE_(N) 20.1 20.7 21.9 20.1 22.1 18.719.2 24.6 23.8 MD₃₀ 10.3 0.9 −30.2 5.4 −25.1 −6.1 31.9 −37.3 −34.0 RMCI0.73 0.65 0.61 0.56 0.68 1.00 0.99 0.86 0.83 Yield 43.4 46.6 50.1 48.349.9 33.5 25.6 53.5 65.6 Tensile 90.2 93.0 102.7 118.2 104.9 81.5 78.9106.0 115.6 % E 48 47 48 48 52 58.5 60 47 52

Table 2 also shows a raw material cost index (RMCI), which compares thematerial costs for each ahoy to that of Comparative Alloy S32100. TheRMCI was calculated by multiplying the average October 2009 cost for theraw materials Fe, Cr, Mn, Ni, Mo, Cu, Nb, and Ti by the percent of eachelement contained in the alloy and dividing by the cost of the rawmaterials in Comparative May S32100. As the calculated values show,Experimental Alloys 6-10 have an RMCI of less than or equal to 0.73,which means the cost of the raw materials contained therein are lessthan or equal to 73% of those in Comparative May S32100. That a materialthat is a suitable alternative to Comparative May S32100 could be madeat a significantly lower raw material cost is surprising and unexpected.

The mechanical properties of Experimental Mays 6-10 have been measuredand compared to Comparative Alloys S32100 and T216Cb. The measured yieldstrength, tensile strength, and percent elongation over a 2-inch gagelength are shown in Table 2. The tensile tests were conducted on 0.100″gage material. All tests were performed at room temperature. Units forthe data in Table 2 are as follows: yield strength and tensile strength,ksi; elongation, percent. As can be seen from the data, the ExperimentalAlloys 6-10 exhibited yield strength and tensile strength significantlybetter than for Comparative Alloy S32100 despite their substantiallyreduced levels of Ni. The amount of increase in yield strength comparedto Comparative Alloy S32100 is surprising and was not anticipated fromthe prior art. The Experimental Alloys also included significantly lessMo than in Comparative May T216Cb. The significantly lower concentrationof the costly alloying elements Ni and Mo is such that the RMCI ofExperimental Alloys 9 and 10 are at least 32% less than the RMCI forComparative May S32100.

The potential uses of these new alloys are numerous. As described andevidenced above, the austenitic stainless steel compositions describedherein are capable of replacing S32100 in many applications.Additionally, due to the high cost of Ni, a significant cost savingswill be recognized by switching from S32100 to the inventive alloycomposition. Another benefit is that because these alloys are fullyaustenitic, they will not be susceptible to either a sharpductile-to-brittle transition (DST) at sub-zero temperature or 885° F.embrittlement at elevated temperatures. Therefore, unlike duplex alloys,they can be used at temperatures above 650° F. and are prime candidatematerials for low temperature and cryogenic applications. Specificarticles of manufacture for which the alloys according to the presentdisclosure would be particularly advantageous include, for example,flexible connectors for automotive exhaust and other applications,bellows, flexible pipe, and chimney/flue liners. Those having ordinaryskill may readily manufacture these and other articles of manufacturefrom the alloys according to the present disclosure using conventionalmanufacturing techniques.

Although the foregoing description has necessarily presented only alimited number of embodiments, those of ordinary skill in the relevantart will appreciate that various changes in the apparatus and methodsand other details of the examples that have been described andillustrated herein may be made by those skilled in the art, and all suchmodifications will remain within the principle and scope of the presentdisclosure as expressed herein and in the appended claims. It isunderstood, therefore, that the present invention is not limited to theparticular embodiments disclosed or incorporated herein, but is intendedto cover modifications that are within the principle and scope of theinvention, as defined by the claims, it will also be appreciated bythose skilled in the art that changes could be made to the embodimentsabove without departing from the broad inventive concept, thereof.

What is claimed is:
 1. An austenitic stainless steel consisting of, inweight percentages: up to 0.20 C; greater than 4.0 to 9.0 Mn; less than1.0 Si; 18.0 to 23.0 Cr; 1.0 to less than 6.0 Ni; up to 3.0 Mo; 0.05 to0.35 N;(7.5(C))≦(Nb+Ti+V+Ta+Zr)≦1.5; greater than 0.0005 to 0.01 B; Fe; andincidental impurities; and wherein the austenitic stainless steel has ayield strength from 43.4 to 53.7 ksi.
 2. The austenitic stainless steelof claim 1, having a PRE_(N) value greater than
 18. 3. The austeniticstainless steel of claim 1, having a PRE_(N) value greater than 18 up to24.
 4. The austenitic stainless steel of claim 1, having a ferritenumber less than
 12. 5. The austenitic stainless steel of claim 1,having a ferrite number greater than 0 up to
 10. 6. The austeniticstainless steel of claim 1, having a ferrite number in the range of 1 upto
 4. 7. The austenitic stainless steel of claim 1, having a MD₃₀ valueof less than 34° C.
 8. The austenitic stainless steel of claim 1, havinga MD₃₀ value less than 10° C.
 9. The austenitic stainless steel of claim1, having a MD₃₀ value less than −10° C.
 10. The austenitic stainlesssteel of claim 1, wherein the yield strength is greater than a yieldstrength of UNS S31635 alloy.
 11. The austenitic stainless steel ofclaim 1, wherein the yield strength is greater than a yield strength ofUNS S32100.
 12. The austenitic stainless steel of claim 1, wherein the Cis limited to up to 0.10.
 13. The austenitic stainless steel of claim 1,wherein the Mn is limited to greater than 4.0 to 8.0.
 14. The austeniticstainless steel of claim 1, wherein the Mn is limited to greater than4.0 to 7.0.
 15. The austenitic stainless steel of claim 1, wherein theSi is limited to 0.2 to 0.5.
 16. The austenitic stainless steel of claim1, wherein the Cr is limited to 18.0 to 22.0.
 17. The austeniticstainless steel of claim 1, wherein the Ni is limited to 2.0 to lessthan 6.0.
 18. The austenitic stainless steel of claim 1, wherein the Niis limited to 3.0 to less than 6.0.
 19. The austenitic stainless steelof claim 1, wherein the Mo is limited to 0.1 to 1.0.
 20. The austeniticstainless steel of claim 1, wherein the Mo is limited to 0.1 to 0.5. 21.The austenitic stainless steel of claim 1, wherein:(7.5(C))≦(Nb+Ti+V+Ta+Zr)≦1.0.
 22. The austenitic stainless steel ofclaim 1, wherein the steel includes at least 0.1 Nb.
 23. The austeniticstainless steel of claim 1, wherein the steel includes at least 0.5 Nb.24. The austenitic stainless steel of claim 1, wherein the steelincludes at least 0.7 Nb.
 25. The austenitic stainless steel of claim 1,wherein(7.5(C))≦Nb≦1.5.
 26. The austenitic stainless steel of claim 1, whereinthe Ti is limited to 0.001 to 0.5.
 27. The austenitic stainless steel ofclaim 1, wherein the B limited to 0.001 to 0.003.
 28. An austeniticstainless steel consisting of, in weight percentages: up to 0.10 C;greater than 4.0 to 8.0 Mn, less than 1.0 Si; 18.0 to 22.0 Cr; 1.0 toless than 6.0 Ni; 0.10 to 2.0 Mo; 0.08 to 0.30 N;(7.5(C))≦(Nb+Ti+V+Ta+Zr)≦1.5; greater than 0.0005 to 0.008 B; up to 0.01Ti; up to 0.050 P; up to 0.030 S; Fe; and incidental impurities; andwherein the austenitic stainless steel has a yield strength from 43.4 to53.7 ksi.
 29. The austenitic stainless steel of claim 28, wherein thesteel includes at least 0.5 Nb.
 30. The austenitic stainless steel ofclaim 28, wherein(7.5(C))≦Nb≦1.5.
 31. An austenitic stainless steel consisting of, inweight percentages: up to 0.08 C; greater than 4.0 to 6.5 Mn; less than1.0 Si; 18.0 to 21.0 Cr; 3.0 to less than 6.0 Ni; 0.1 to 1.0 Mo; 0.08 to0.30 N;(7.5(C))≦(Nb+Ti+V+Ta+Zr)≦1.0; greater than 0.0005 to 0.005 B; up to0.005 Ti; up to 0.035 P; up to 0.005 S; Fe; and incidental impurities;and wherein the austenitic stainless steel has a yield strength from43.4 to 53.7 ksi.
 32. An article of manufacture including an austeniticstainless steel as recited in claim
 1. 33. The article of manufacture ofclaim 32, wherein the article is selected from the group consisting of aflexible connector, a bellows, a flexible pipe, a chimney liner, and aflue liner.